Ruby is the Hardest


RUBY EXIT

 

 

Ruby and Sapphire are the hardest among the materials selected for coil winding nozzle entrance and exit. Their single crystal (mono crystalline) structure allows diamond polishing to a mirror finish unmatched by other material, reducing friction and protecting the wire.  Shown at left is a photomicrograph of a ruby exit orifice.

 


Technical Data


          Hardness value: 1,800 – 2,200 Vickers, or 3 times that of case hardened steel

 

          Surface roughness: 0.025 – 0.05 microns, or 1 – 2 micro inches Ra

 

          Tip I. D. Choice of  Ø 0.3, 0.5, 0.6, 0.7, 0.8, 1.0, 1.2, 1.4, 1.8 mm

 

          Outside diameter: 0.5 – 4.0 mm, wall thickness governing

 

          Length: 10 – 50 mm, aspect ratio governing

 

          Young's modulus: 190 - 210 MPa

 

Issues with Ruby Tipped Nozzle

The body of a ruby tipped nozzle is usually made of a stainless steel tube that retains the longitudinal grains inherent to all hard drawn steel tubes, which will form a bulge in the bore when bent then straightened. Upon impact, the ruby tip either will be broken or fractured which may not be visible to the naked eyes but which nevertheless will damage the wire. Therefore, a ruby nozzle after impact should be discarded.

 